New Type Tundish Alkaline Refractories Dry Vibration Mix And Tundish Inner Lining And Permanent Coating

Chat Now
Product Details

Quick Details

 Place of Origin:  Henan, China (Mainland)
 Shape:  Powder
 Material:  CaO,SiO2,MgO
 SiO2 Content (%):  min 79
 CaO Content (%):  min 17
 MgO%:  min 79
 Refractoriness (Degree):  1770°< Refractoriness< 2000°
 Brand Name:  Topchase
 Bulk density/ g/cm3:  min 2.3-2.59
 LCR %:  ±0.1~±0.13
 MOR /Mpa:  min 3.9
 Initial sintering temp ℃:  1000
 Max . service temp ℃:  1700
 Payment:  LC,TT,DP,West Union
 Application:  Used for tundish lining
 Brad name: Topchase

Packaging & Delivery

Packaging Details: 25kg/bag, wooden pallets with plastic film
Delivery Detail: 10-30 days according to the order quantity

Product details
The advanced Tundish refractories dry vibration mix composed of electro fused magnesite and dead burnt magnesite were tested successfully in several steel-making factories. what the Liner Dry vibration Mix impresses most is its long service life and easy to bake, which is impossible be paralleled by other coating material.

Features
 1.Its service life is up to 55 hours.
 2.Greatly improve the tundish using life.
 3. Easy to operate and bake.
 4.Reduce the consumption of labor power.
 5.Can be applied in any climatic condition.

Specification

Item

2G-1

2G-2

Chemical composition  (MgO) %

≥ 85

≥ 90

Grain size  (mm)

5

5

Bulk density  (g/cm 3)

≥ 2.3

≥ 2.5

Compressive strength  Mpa (1500 ℃x3h)

≥ 1.5

≥1.7

Linear changing rate  (%)

-0.09

-0.01

Suggested working mode

continuously

continuously

Application

Alkaline material smelting, such as carbon steel, high manganese steel, etc. Especially for manganese alloy series smelting.

Packing

Tundish Lining Development History:
 1) Before 1995, lining is Siliceous heat-insulating board,and average service life is from 6hr to10 hr. It has poor erosion resistance and pollution on ladle.
 2) After 1995, people replaced the siliceous board with Magnesia calcium or magnesium coating as the tundish liner. The service life improved, up to about 24 hrs which could purify the ladle. However, it heavily increased the demand for mechanical spraying or manual labor daubing.

3)Since 2000, with the rapid development of Tundish rapid replacement technology, the tundish service life has been greatly improved,which will also have more higher requirement on the liner.


If you are looking high quality and hot sale new type tundish alkaline refractories dry vibration mix and tundish inner lining and permanent coating at low price, you can feel free to contact our company - Topchase Metallurgical, one of the leading manufacturers and suppliers in China. We can supply you with special offer customized new type tundish alkaline refractories dry vibration mix and tundish inner lining and permanent coating in stock.